废旧电路板低温改性研究

摘要： 介绍了电路板的组成和类型,重点研究了废旧电路板在低温状态下冲击强度、弯曲强度和剪切强度的改性变化.实验结果表明,冲击强度和剪切强度在-30℃时变化明显.在此基础上进行了粗碎实验和细碎实验,先使用ZKB-2型双辊式剪切破碎机将电路板破碎到20 mm×20 mm的块状,测试在低温状态下的功耗并计算其生产能力,在-30℃～-10℃范围内,生产能力可提高约17%,再降低温度会使产品质量受到影响.然后使用R型冲击破碎机对废旧电路板进行细碎实验,将物料破碎到3 mm以下,并记录在不同工况下的参数.实验结果表明在-30℃左右平均功率下降得较快,冷却5min对低温改性最有利. Abstract： Introduce cryogenic grinding and the components of Printed Circuit Board (PCB). Study the low-temperature modification of PCB, including mechanical property to find the influence of the different low-temperature on impact strength, flexural strength, shear strength of PCB. Tests show that impact strength and shear strength of PCB change sharply at -30℃. Used ZKB-2 type double roll shear crusher to crush PCB to 20mm×20mm particle size, in a temperature range of -30℃～ -10℃, the product yield is 17% higher than room temperature, and much lower temperature may deteriorate the product quality of crusher. Used R type mill to grind sample to minus 3mm under different working condition, the average power is decrease in evidence at -30℃, freezing time for 5 minutes is best. 作 者： 周翠红    路迈西    潘永泰    陈茂和    乔雪峰    ZHOU Cui-hong    LU Mai-xi    PAN Yong-tai    CHEN Mao-he    QIAO Xue-feng   作者单位： 周翠红,乔雪峰,ZHOU Cui-hong,QIAO Xue-feng(北京石油化工学院环境工程系,北京,102617)

路迈西,潘永泰,陈茂和,LU Mai-xi,PAN Yong-tai,CHEN Mao-he(中国矿业大学北京校区化学与环境工程学院,北京,100083) 

期 刊： 中山大学学报(自然科学版)  ISTICPKU   Journal： ACTA SCIENTIARUM NATURALIUM UNIVERSITATIS SUNYATSENI  年，卷(期)： 2007, 46(z1)  分类号： X705  关键词： 电路板    低温改性    破碎    细碎    Keywords： printed circuit board (PCB)    low-temperature modification    crush    grind   

【废旧电路板低温改性研究】上海花千坊相关的文章：

[品牌]改性塑料项目可行性研究报告04-28

让废旧电池回家02-26

废旧电池的危害作文09-21

让废旧电池回家作文09-13

废旧电池不能乱扔作文12-10

焊接电路板心得体会03-14

环保教案《废旧电池回收》04-25

回收废旧电池倡议书11-10

【精选】废旧电池的危害作文9篇02-24

奇妙的动物车中班废旧材料教案08-25